38CrMoALA screw PTA screw Barrel

Brief introduction： 38CrMoAlA nitride, Bimetallic coating on the top of the flights with Ni-based alloy Stellite PTA welding machine from Germany is adopted for hardfacing, with the alloy thickness over 1.5mm, hardness of HRC50~56, providing high surfacing bonding strength, dense textile, and effectively improving the resistance of the screws to abrasion, high temperature and corrosion. It helps extend the service life of the screw. Basic parameters： Hardness of bimetallic layer (HRC): 48-58 Wear resistance: good Corrosion resistance: not very good Scope of application： Resin, plastics with glass fiber content below 15%, with guarantee period of 1 year PC, PMMA, PP, PP fireproof, PS, AS, ABS, PVC, PET, PO, POM, AS, TPU, TPR, TPE, PC+ABS with glass fiber content below 15% Composition and process：

Single Screw For Extrusion Machine HY1 sintered barrel HY1 sintered screw HY1 sintered small piece HK1 Iron Base Bimetallic Barrel